Structural effect of heavy ion irradiation on GdBaCuO ceramics

Abstract : The influence of twin boundaries as sinks on defects induced by 480 keV Kr ion irradiation in GdBaCuO crystals was observed in situ at 40 and 300 K. The interaction of the dislocations with the twin boundaries followed on a video recording. A crystalline to amorphous transition was observed above a total fluence of ∼ 4 - 5 x 10^12 Kr/cm2. A comparison between orthorhombic (Os) crystals and a monoclinic structure (Ms) (close to Os and whose parameters were calculated) shows that the behaviour of irradiation-induced extended defects does not depend on a small initial deformation of the orthorhombic cell. In both case, an occasional orthorhombic (or monoclinic) to tetragonal phase transition only occurs when the amorphization process has begun.
Type de document :
Article dans une revue
Revue de Physique Appliquee, 1990, 25 (1), pp.49-53. <10.1051/rphysap:0199000250104900>


https://hal.archives-ouvertes.fr/jpa-00246161
Contributeur : Archives Journal de Physique <>
Soumis le : lundi 1 janvier 1990 - 08:00:00
Dernière modification le : jeudi 27 mars 2008 - 15:34:59
Document(s) archivé(s) le : lundi 10 mai 2010 - 16:51:25

Fichier

ajp-rphysap_1990_25_1_49_0.pdf
Accord explicite pour ce dépôt

Identifiants

Collections

Citation

M.-O. Ruault, H. Bernas, M. Gasgnier, J.-C. Levet, H. Noel, et al.. Structural effect of heavy ion irradiation on GdBaCuO ceramics. Revue de Physique Appliquee, 1990, 25 (1), pp.49-53. <10.1051/rphysap:0199000250104900>. <jpa-00246161>

Exporter

Partager

Métriques

Consultations de
la notice

115

Téléchargements du document

121