Characterization of Some Physical and Photocatalytic Properties of CuO Nanofilms Synthesized by a Gentle Chemical Technique
Résumé
Pure and Li-doped CuO nanofilms were synthesized on heated glass substrates using the spray-pyrolysis technique. The deposited pure CuO nanofilms were achieved at a precursor molarity of 0.2 M using a solution prepared from copper nitrate trihydrate (Cu(NO3)2·3H2O). Doped Li–CuO nanofilms were obtained using several doping concentrations (3, 6, 9, 12 and 15%) by adding a solution prepared from lithium nitrate (LiNO3). The pure and Li–CuO samples were investigated by different techniques. XRD revealed three dominant peaks (-111), (111) and (211), which are the properties of monoclinic CuO. The increase in Li-doping concentration showed the appearance of other peaks of low intensities detected at 2θ ranging from 49 to 68°. AFM images showed a textured and inhomogeneous surface composed of spherical grains whose size decreased with increasing Li doping. UV–visible spectroscopy showed that the CuO samples were of low transparency; the transmittance was less than 50%. The band-gap energy determined from Tauc’s equation plot increased from 2.157 to 3.728 eV with the increase in Li doping. These values correspond well to the band gap of semiconducting CuO. The photocatalytic properties were accelerated by Li doping, as revealed by the discoloration of aqueous methylene-blue (MB) solution under ultraviolet irradiation.
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Licence : CC BY - Paternité
Licence : CC BY - Paternité