Electrophoretic deposition of aluminum particles from pure propan-2-ol suspensions

Julien Wagner (1, 2) , Claudie Josse (3) , Léa Gani (2) , Stéphane Knittel (2) , Pierre-Louis Taberna (1) , Florence Ansart (1)

1 CIRIMAT - Centre interuniversitaire de recherche et d'ingenierie des matériaux
2 Safran Aircraft Engines
3 Centre Castaing - Centre de microcaractérisation Raimond Castaing

Aluminum (Al) coatings were deposited on 15CDV6 steel substrates using the electrophoretic deposition (EPD) process and pure propan-2-ol solvent. Key parameters in EPD process are the followings: solvent, additives, deposition conditions, electrical field, cell geometry. Herein, the influence of the applied electric field (0–60 Vcm−1) and the deposition time (0–20 min) was precisely studied as a function of the deposition rate. A uniform and porous Al particle coating was targeted and obtained. Control of the deposit thickness with conservation of the microstructure was possible over a large range of electric fields and deposition times. No thickness limitation was observed in the investigated range of deposition times and electric fields without the need of any added ionic species. Besides, voltage measurements showed that the electric field over the suspension during the EPD process remains high, allowing continuous migration of Al particles to the coated electrode. Overall, the EPD process turned out to be an efficient way to adjust the deposit thicknesses up to 200 μm.

Mots clés: Electrophoretic deposition process; Aluminum particles; Deposition parameters; Microstructure; Homogeneous coating

Domaines: Matériaux

Julien Wagner, Claudie Josse, Léa Gani, Stéphane Knittel, Pierre-Louis Taberna, et al.. Electrophoretic deposition of aluminum particles from pure propan-2-ol suspensions. Results in Materials, 2022, 13, pp.100259. ⟨10.1016/j.rinma.2022.100259⟩. ⟨hal-03880261⟩