Empirical propagation laws of intergranular corrosion defects affecting 2024 T351 alloy in chloride solutions
Résumé
In the present work, a first attempt was made to determine propagation laws of intergranular corrosion defects for Al 2024 T351 in various NaCl solutions as a first step for future predictive modeling of 2024 alloy. In a first step, the effect of chloride concentration on the susceptibility to intergranular corrosion of 2024 alloy was studied using current–potential curves. In a second step, conventional immersion tests were performed in chloride-containing solutions and statistical analysis was carried out to determine the depth of the intergranular corrosion defects, depending on the chloride concentration and on the immersion time. The results were compared to those obtained by measuring the load to failure of precorroded tensile specimens versus preimmersion time in a chloride solution. The latter method was selected to measure the depth of the intergranular defects even though results showed that it was not possible to use it for chloride concentrations higher than 3 M and immersion times longer than 1200 h, considering the chloride concentrations and the durations of immersion studied in this work. Thus, empirical propagation laws are proposed for chloride contents as high as 3 M and immersion times as long as 1200 h.
Origine : Fichiers produits par l'(les) auteur(s)