Strain-induced crystallization of poly(ethylene 2,5-furandicarboxylate). Mechanical and crystallographic analysis

Abstract : Poly(ethylene 2,5-furandicarboxylate), referred to as PEF, was uni-axially stretched for temperatures above glass transition temperature. This bio-based polymer is considered as a serious competitor for the petroleum analogous poly(ethylene terephthalate), named PET. To replace PET in bottle forming, PEF has to be deformed to large strains which are only reachable when it is in its rubbery state. In the present work, the stretching conditions have been chosen by determining precisely the range of temperature and strain rate where PEF exhibits a rubbery-like state. This was feasible through the building of a master curve at a reference temperature. Local strain field measurements allow the description of PEF intrinsic mechanical behaviour. Above a draw ratio of around 6 to 8, the mechanical response presents an impressive strain hardening whereas a well-defined crystalline phase with a high orientation is formed. Diffraction peaks were indexed and compared to previous papers. Only one crystalline phase was observed either under mechanical loading or during static crystallization. Mechanical loading significantly speeds up crystallization.
Document type :
Journal articles
Complete list of metadata

Cited literature [39 references]  Display  Hide  Download

https://hal.archives-ouvertes.fr/hal-02429039
Contributor : Christelle Combeaud Connect in order to contact the contributor
Submitted on : Tuesday, January 14, 2020 - 4:54:03 PM
Last modification on : Wednesday, November 17, 2021 - 12:28:38 PM
Long-term archiving on: : Wednesday, April 15, 2020 - 12:31:08 PM

File

VF.pdf
Publisher files allowed on an open archive

Identifiers

Citation

Emilie Forestier, Christelle Combeaud, Nathanaël Guigo, Gabriel Monge, Jean-Marc Haudin, et al.. Strain-induced crystallization of poly(ethylene 2,5-furandicarboxylate). Mechanical and crystallographic analysis. Polymer, Elsevier, 2020, 187, ⟨10.1016/j.polymer.2019.122126⟩. ⟨hal-02429039⟩

Share

Metrics

Record views

220

Files downloads

606