Tensile strength of aligned discontinuous composites
Résistance en traction d'un composite unidirectionnel à renforts discontinus
Résumé
Recycled carbon fibres allows creating a unidirectional tape composed of aligned and discontinuous tows. Composites made from this semi-product have promising, but still scattered mechanical properties. The stress-transfer between tows is a key factor affecting the strength of these composites. In order to understand this mechanism, plates were manufactured with interrupted unidirectional plies. Double overlap architectures allow defining the main properties of the interface, based on a simplified expression of the energy release rate. Finally the strength of single overlap architectures was compared with Abaqus numerical predictions.
L’utilisation de fibres de carbone recyclées offre l’opportunité de réaliser un semi produit sous la forme d’une bande unidirectionnelle constituée de mèches alignées et discontinues. Les composites réalisés à partir de ce semi produit présentent actuellement des propriétés mécaniques prometteuses, mais avec une dispersion encore trop importante. Le transfert de charge entre mèches constitue un facteur clé de la résistance mécanique de ces composites. Afin d’appréhender ce mécanisme, des plaques sont réalisées avec des plis unidirectionnels coupés. Des architectures à double recouvrement permettent d’identifier les principales propriétés de l’interface, en s’appuyant sur une expression simplifiée du taux de restitution d’énergie. Enfin, la résistance d’architectures à simple recouvrement sont comparées avec des prédictions numériques effectuées sur Abaqus.
Fichier principal
JNC21_YANG_Resistance_en_traction_d_un_composite_unidirectionnel_a_renforts_discontinus.pdf (1.09 Mo)
Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...