Thermodynamic analysis of the breathing of amino-functionalized MIL-53(Al) upon CO2 adsorption

Abstract : Carbon dioxide gas adsorption in amino-functionalized MIL-53(Al) at various temperatures has been analysed in combination with temperature programmed XRD. Similarly to the regular MIL-53(Al) material, the so-called breathing phenomenon was shown to take place in the amino-MIL-53 upon adsorption of different molecules, i.e. the transition between a large-pore (lp) and a narrow-pore (np) structure. Using the osmotic thermodynamic model analysis, the temperature–loading phase diagram was derived. The overall diagram is similar to that for the regular MIL-53(Al), but a spectacular difference is the much larger stability domain of the np structure, which can be accounted for by the increased affinity for CO2 due to the presence of the amino groups in the pore space.
Complete list of metadatas

https://hal.archives-ouvertes.fr/hal-02142935
Contributor : François-Xavier Coudert <>
Submitted on : Wednesday, May 29, 2019 - 12:16:04 AM
Last modification on : Tuesday, June 4, 2019 - 1:42:05 AM

File

postprint.pdf
Files produced by the author(s)

Identifiers

Citation

Anne Boutin, Sarah Couck, François-Xavier Coudert, Pablo Serra-Crespo, Jorge Gascon, et al.. Thermodynamic analysis of the breathing of amino-functionalized MIL-53(Al) upon CO2 adsorption. Microporous and Mesoporous Materials, Elsevier, 2011, 140 (1-3), pp.108-113. ⟨10.1016/j.micromeso.2010.07.009⟩. ⟨hal-02142935⟩

Share

Metrics

Record views

6

Files downloads

2