Prediction of failure in bending of an aluminium sheet alloy
Résumé
This work is dedicated to numerical prediction of the bending of thin aluminium alloy sheets, with a focus on the material parameter identification and the prediction of rupture with or without pre-strains in tension prior to bending. The experimental database consists of i) mechanical tests at room temperature, such as tension and simple shear, performed at several orientations to the rolling direction and biaxial tension air bending tests of rectangular samples after (or not) pre-straining in tension. The mechanical model is composed of the Y1d2004-18p anisotropic yield criterion (Barlat et al. [3]) associated with a mixed hardening rule. The material parameters (altogether 21) are optimized with an inverse approach, in order to minimize the gap between experimental data and model predictions. Then, the Hosford-Coulomb rupture criterion is used in an uncoupled way, and the parameters are determined from tensile tests, both uniaxial and biaxial, with data up to rupture. In a second step, numerical simulations of the bending tests are performed, either on material in its original state or after pre-straining in tension, with pre-strain magnitudes increasing from 0.19 up to 0.3. The comparisons are performed on different outputs load evolution, strain field and prediction of the rupture. A very good correlation is obtained over all the tests, in the identification step as well as in the validation one. Moreover, the fracture criterion proves to be successful whatever the amount of pre-strain may be. A convincing representation of the mechanical behavior at room temperature for an aluminium alloy is thus obtained.