Electrical behavior of a graphene/PEKK and carbon black/PEKK nanocomposites in the vicinity of the percolation threshold

Abstract : Graphene and carbon black have been dispersed in a high performance thermoplastic polymer, the poly(ether ketone ketone), to improve its electrical conductivity. The dispersion of graphene has a significant influence on the percolation threshold. A simple exfoliation protocol to obtain graphene monolayers has led to a significant decrease of the percolation threshold from 4.2 to 1.9 vol%. To the best of our knowledge, it is one of the lowest percolation values for unfunctionalized graphene dispersed by melt blending in a high performance thermoplastic matrix. The conductivity value above the percolation threshold (1.2 S·m−1) means that graphene was not degraded during the elaboration process. Below the percolation threshold, Maxwell-Wagner-Sillars phenomenon increases the dielectric permittivity from 2.7 to 210 for PEKK/6 vol% graphene at 180 °C and 1 Hz. Dynamic mechanical analyses have shown that mechanical moduli were not significantly modified by conductive particles until 6 vol%.
Document type :
Journal articles
Complete list of metadatas

Cited literature [3 references]  Display  Hide  Download

https://hal.archives-ouvertes.fr/hal-02073556
Contributor : Open Archive Toulouse Archive Ouverte (oatao) <>
Submitted on : Wednesday, March 20, 2019 - 8:35:32 AM
Last modification on : Friday, June 14, 2019 - 6:31:23 PM
Long-term archiving on : Friday, June 21, 2019 - 12:51:55 PM

File

 Restricted access
To satisfy the distribution rights of the publisher, the document is embargoed until : 2019-09-14

Please log in to resquest access to the document

Identifiers

Citation

Camille Bessaguet, Eric Dantras, Guilhem Michon, Mathieu Chevalier, Lydia Laffont, et al.. Electrical behavior of a graphene/PEKK and carbon black/PEKK nanocomposites in the vicinity of the percolation threshold. Journal of Non-Crystalline Solids, Elsevier, 2019, 512, pp.1-6. ⟨10.1016/j.jnoncrysol.2019.02.017⟩. ⟨hal-02073556⟩

Share

Metrics

Record views

26