On calorimetric study of the fragility in bulk metallic glasses with low glass transition temperature: (Ce0.72Cu0.28) 90-x Al10Fex (x = 0, 5 or 10) and Zn 38Mg12Ca32Yb18

Abstract : Compared with conventional bulk metallic glasses, Ce-based and Zn-based bulk metallic glasses have received considerable attention because of their possible application as structural and functional materials. Kinetic fragility parameter m in amorphous material presents degree of deviations from the Arrhenius law above the glass transition temperature (Tg) of the material. Kinetic fragility parameter (m) and Kauzmann temperature (T K) in (Ce0.72Cu0.28)90-x Al 10Fex (x = 0, 5 or 10) and Zn38Mg 12Ca32Yb18 bulk metallic glasses have been determined by differential scanning calorimetry (DSC). Results show that Zn 38Mg12Ca32Yb18 presents a higher m than (Ce0.72Cu0.28)90-x Al10Fe x (x = 0, 5 or 10). The activation energies Eg for glass transition are 1.51 eV (x = 0), 1.59 eV (x = 5) and 1.83 eV (x = 10) in (Ce 0.72Cu0.28)90-x Al10Fex (x = 0, 5 or 10), and 3.59 eV in Zn38Mg12Ca 32Yb18, respectively. The values of Eg increase with increasing the Fe content in (Ce0.72Cu0.28) 90-x Al10Fex (x = 0, 5 or 10) bulk metallic glasses. Kinetic fragility parameter m of bulk metallic glasses increases with the glass transition temperature Tg of bulk metallic glasses, in agreement with previous investigations. © 2011 Elsevier Ltd. All rights reserved.
Type de document :
Article dans une revue
Intermetallics, Elsevier, 2011, 19 (10), pp.1367-1373. 〈10.1016/j.intermet.2011.04.008〉
Liste complète des métadonnées

https://hal.archives-ouvertes.fr/hal-01813690
Contributeur : Laboratoire Mateis <>
Soumis le : mardi 12 juin 2018 - 15:20:42
Dernière modification le : samedi 27 octobre 2018 - 01:20:46

Identifiants

Collections

Citation

J.C. Qiao, Jean-Marc Pelletier, Q. Wang, W. Jiao, W.H. Wang. On calorimetric study of the fragility in bulk metallic glasses with low glass transition temperature: (Ce0.72Cu0.28) 90-x Al10Fex (x = 0, 5 or 10) and Zn 38Mg12Ca32Yb18. Intermetallics, Elsevier, 2011, 19 (10), pp.1367-1373. 〈10.1016/j.intermet.2011.04.008〉. 〈hal-01813690〉

Partager

Métriques

Consultations de la notice

51