Effect of void arrangement on ductile damage mechanisms in nodular graphite cast iron: In situ 3D measurements

Abstract : The effect of the arrangement of two artificial voids on void growth and coalescence mechanisms is studied in flat specimens made of nodular graphite cast iron via in situ 3D laminography imaging and digital volume correlation for bulk displacement measurement. Two configurations of machined holes are studied i) 90° with respect to the loading direction to mimic internal necking, and ii) 45° to attempt to trigger a void sheeting mechanism between the artificial voids. The machined holes play the role of primary voids, the graphite nodules that of secondary voids. At a lower scale there is a smaller third population of voids. The 45° void orientation successfully causes a shear band between the primary voids. However, the growth and coalescence mechanisms of voids from graphite nodules are similar for the two configurations. Internal necking is found for nodules that are close to each other and void sheeting for large ferrite ligaments between nodules. Strain fields in the region between machined holes show necking for both cases as well as volume increase, i.e., positive trace of the strain tensor, confirmed by image analysis. The strain to failure in this inter-void region is evaluated in the bulk and also locally, between nodules and for different coalescence configurations. Similar levels are observed in both cases.
Type de document :
Article dans une revue
Engineering Fracture Mechanics, Elsevier, 2018, 192, pp.242-261. 〈10.1016/j.engfracmech.2018.01.008〉
Liste complète des métadonnées

https://hal.archives-ouvertes.fr/hal-01710087
Contributeur : François Hild <>
Soumis le : mardi 27 mars 2018 - 15:44:14
Dernière modification le : lundi 12 novembre 2018 - 11:03:54
Document(s) archivé(s) le : jeudi 13 septembre 2018 - 09:14:47

Fichier

EFM2018b-ccsd.pdf
Fichiers produits par l'(les) auteur(s)

Identifiants

Citation

Ante Buljac, Lukas Helfen, François Hild, Thilo Morgeneyer. Effect of void arrangement on ductile damage mechanisms in nodular graphite cast iron: In situ 3D measurements. Engineering Fracture Mechanics, Elsevier, 2018, 192, pp.242-261. 〈10.1016/j.engfracmech.2018.01.008〉. 〈hal-01710087〉

Partager

Métriques

Consultations de la notice

155

Téléchargements de fichiers

50