Thermosensitive polymer-grafted iron oxide nanoparticles studied by in situ dynamic light backscattering under magnetic hyperthermia

Gauvin Hemery (1, 2) , Elisabeth Garanger (1, 2) , Sébastien Lecommandoux (1, 2) , Andrew Wong (3) , Elizabeth Gillies (3) , Boris Pedrono (4) , Thomas Bayle (4) , David Jacob (4) , Olivier Sandre (1, 2)

1 LCPO - Laboratoire de Chimie des Polymères Organiques
2 Team 3 LCPO : Polymer Self-Assembly & Life Sciences
3 UWO - University of Western Ontario
4 Cordouan Technologies

Thermometry at the nanoscale is an emerging area fostered by intensive research on nanoparticles (NPs) that are capable of converting electromagnetic waves into heat. Recent results suggest that stationary gradients can be maintained between the surface of NPs and the bulk solvent, a phenomenon sometimes referred to as ` cold hyperthermia'. However, the measurement of such highly localized temperatures is particularly challenging. We describe here a new approach to probing the temperature at the surface of iron oxide NPs and enhancing the understanding of this phenomenon. This approach involves the grafting of thermosensitive polymer chains to the NP surface followed by the measurement of macroscopic properties of the resulting NP suspension and comparison to a calibration curve built up by macroscopic heating. Superparamagnetic iron oxide NPs were prepared by the coprecipitation of ferrous and ferric salts and functionalized with amines, then azides using a sol-gel route followed by a dehydrative coupling reaction. Thermosensitive poly[2-(dimethylamino) ethyl methacrylate] (PDMAEMA) with an alkyne end-group was synthesized by controlled radical polymerization and was grafted using a copper assisted azide-alkyne cycloaddition reaction. Measurement of the colloidal properties by dynamic light scattering (DLS) indicated that the thermosensitive NPs exhibited changes in their Zeta potential and hydrodynamic diameter as a function of pH and temperature due to the grafted PDMAEMA chains. These changes were accompanied by changes in the relaxivities of the NPs, suggesting application as thermosensitive contrast agents for magnetic resonance imaging (MRI). In addition, a new fibre-based backscattering setup enabled positioning of the DLS remote-head as close as possible to the coil of a magnetic heating inductor to afford in situ probing of the backscattered light intensity, hydrodynamic diameter, and temperature. This approach provides a promising platform for estimating the response of magnetic NPs to application of a radiofrequency magnetic field or for understanding the behaviour of other thermogenic NPs.

Mots clés: magnetic hyperthermia; dynamic light scattering; light backscattering; radiofrequency magnetic field; sol-gel and click chemistry; CONTRAST AGENTS; magnetic nanoparticles; MRI; CATALYSIS; thermosensitive polymers

Domaines: Polymères; Science des matériaux [cond-mat.mtrl-sci]; Matière Molle [cond-mat.soft]

Gauvin Hemery, Elisabeth Garanger, Sébastien Lecommandoux, Andrew Wong, Elizabeth Gillies, et al.. Thermosensitive polymer-grafted iron oxide nanoparticles studied by in situ dynamic light backscattering under magnetic hyperthermia. Journal of Physics D: Applied Physics, 2015, 48 (49), pp.494001. ⟨10.1088/0022-3727/48/49/494001⟩. ⟨hal-01361281⟩