Synthesis, characterization and electrical properties of La0.7Sr0.3Co0.2Fe0.8O3/Gd-CeO2 thin films (<= 500 nm)

Abstract : A simple route toward the synthesis of mesostructured composite La(0.7)Sr(0.3)Co(0.2)Fe(0.8)O(3)x/yGd-CeO2 (LSCFx/ yGDC) (with x and y representing the volumetric% of LSCF and GDC in the composite films) thin films exhibiting both high electrical conductivities and optimized bicontinuous pore-solid network is reported. Because of the size of the pore wall, the mesostructured composite film is crystalline with particle size in the nanometer range even after a heat-treatment at 700 degrees C in air. Crystallization of the film was studied by in situ impedance spectroscopy. This technique allows us to define the heattreatment, the LSCF content in the composite film and the thickness of the film to achieve good electrical conductivity. The highest electrical conductivity of 250 S cm(-1) was found for the pure, mesoporous LSCF film at 700 degrees C.
Document type :
Journal articles
Complete list of metadatas

https://hal.archives-ouvertes.fr/hal-01289929
Contributor : Gestionnaire Hal-Upmc <>
Submitted on : Thursday, March 17, 2016 - 2:16:15 PM
Last modification on : Tuesday, September 22, 2020 - 3:40:17 AM

Identifiers

Citation

Guillaume Muller, Armelle Ringuedé, Christel Laberty-Robert. Synthesis, characterization and electrical properties of La0.7Sr0.3Co0.2Fe0.8O3/Gd-CeO2 thin films (<= 500 nm). Journal of Materials Chemistry A, Royal Society of Chemistry, 2014, 2 (18), pp.6448-6455. ⟨10.1039/c3ta14505k⟩. ⟨hal-01289929⟩

Share

Metrics

Record views

176