Er3+-Al2O3 nanoparticles doping of borosilicate glass

Abstract : Novel borosilicate glasses were developed by adding in the glass batch Er3+–Al2O3 nanoparticles synthetized by using a soft chemical method. A similar nanoparticle doping with modified chemical vapour deposition (MCVD) process was developed to increase the efficiency of the amplifying silica fibre in comparison to using MCVD and solution doping. It was shown that with the melt quench technique, a Er3+–Al2O3 nanoparticle doping neither leads to an increase in the Er3+ luminescence properties nor allows one to control the rare-earth chemical environment in a borosilicate glass. The site of Er3+ in the Er3+–Al2O3 nanoparticle containing glass seems to be similar as in glasses with the same composition prepared using standard raw materials. We suspect the Er3+ ions to diffuse from the nanoparticles into the glass matrix. There was no clear evidence of the presence of Al2O3 nanoparticles in the glasses after melting.
Document type :
Journal articles
Complete list of metadatas

https://hal.archives-ouvertes.fr/hal-01228087
Contributor : Stéphane Toulin <>
Submitted on : Thursday, November 12, 2015 - 3:55:19 PM
Last modification on : Tuesday, June 30, 2020 - 4:42:10 PM

Links full text

Identifiers

Collections

Citation

Jonathan Massera, Laëtitia Petit, Joona Koponen, Benoit Glorieux, Leena Hupa, et al.. Er3+-Al2O3 nanoparticles doping of borosilicate glass. Bulletin of Materials Science, Indian Academy of Sciences, 2015, 38 (5), pp.1407-1410. ⟨10.1007/s12034-015-1028-3⟩. ⟨hal-01228087⟩

Share

Metrics

Record views

138