Modelling the transverse viscoelasticity of green wood using a combination of two parabolic elements
Résumé
The rigidity in radial compression at different levels of temperature and strain rate have
been measured on green Boco, with a drastic softening around 60◦C attributed to the
glassy transition of lignin. The representation of experimental results in an approximated
complex diagram revealed a secondary viscoelastic process occurring at lower temperature.
A multiparabolic model was used for the analysis. For convenience, each parabolic
element was replaced by a generalised Maxwell model with a modified-Gaussian relaxation
spectrum. This model fitted correctly the observed behaviour of wood in the time range
of 0.05 to 50 sec and temperature between 10 to 90◦C.
Le module de rigidité en compression radiale a été mesuré à différents niveaux de
température et de vitesse de sollicitation sur des échantillons de Boco à l’état vert. La chute
importante du module autour de 60◦C est attribuée à la transition vitreuse des lignines. La
représentation des résultats expérimentaux dans un plan complexe approché fait apparaître
un deuxième mécanisme viscoélastique à basse température. Un modèle biparabolique
permet d’interpréter les résultats. Chaque élément parabolique est remplacé par un modèle
de Maxwell généralisé avec spectre quasi-gaussien des rigidités. Ce modèle représente
correctement le comportement du bois observé expérimentalement pour une plage de temps
comprise entre 0,05 s et 50 s et pour une température comprise entre 10 et 90◦C.