Structural and optical characterization of pure Si-rich nitride thin films

Abstract : The specific dependence of the Si content on the structural and optical properties of O-and H-free Si-rich nitride (SiN x>1.33) thin films deposited by magnetron sputtering is investigated. A semiempirical relation between the composition and the refractive index was found. In the absence of Si-H, N-H, and Si-O vibration modes in the FTIR spectra, the transverse and longitudinal optical (TO-LO) SiN stretching pair modes could be unambiguously identified using the Berreman effect. With increasing Si content, the LO and the TO bands shifted to lower wavenumbers, and the LO band intensity dropped suggesting that the films became more disordered. Besides, the LO and the TO bands shifted to higher wavenumbers with increasing annealing temperature which may result from the phase separation between Si nanoparticles (Si-np) and the host medium. Indeed, XRD and Raman measurements showed that crystalline Si-np formed upon 1100°C annealing but only for SiN x<0.8. Besides, quantum confinement effects on the Raman peaks of crystalline Si-np, which were observed by HRTEM, were evidenced for Si-np average sizes between 3 and 6 nm. A contrario, visible photoluminescence (PL) was only observed for SiN x>0.9 , demonstrating that this PL is not originating from confined states in crystalline Si-np. As an additional proof, the PL was quenched while crystalline Si-np could be formed by laser annealing. Besides, the PL cannot be explained neither by defect states in the bandgap nor by tail to tail recombination. The PL properties of SiN x>0.9 could be then due to a size effect of Si-np but having an amorphous phase.
Complete list of metadata

Cited literature [58 references]  Display  Hide  Download

https://hal.archives-ouvertes.fr/hal-01138071
Contributor : Julien Cardin <>
Submitted on : Thursday, April 2, 2015 - 4:07:23 PM
Last modification on : Wednesday, September 15, 2021 - 3:14:25 AM
Long-term archiving on: : Thursday, September 10, 2015 - 2:20:40 PM

File

Debieu_NRL_1556-276X-8-31.pdf
Publisher files allowed on an open archive

Identifiers

Citation

Olivier Debieu, Ramesh Pratibha Nalini, Julien Cardin, Xavier Portier, Jacques Perrière, et al.. Structural and optical characterization of pure Si-rich nitride thin films. Nanoscale Research Letters, SpringerOpen, 2013, 8 (1), pp.1-13. ⟨10.1186/1556-276X-8-31⟩. ⟨hal-01138071⟩

Share

Metrics

Record views

863

Files downloads

559