Breathing transitions in MIL-53(Al) metal-organic framework upon xenon adsorption.

Anne Boutin (1) , Marie-Anne Springuel-Huet (2) , Andrei Nossov (2) , Antoine Gedeon (2) , Thierry Loiseau (3) , Christophe Volkringer (3) , Gérard Férey (3) , François-Xavier Coudert (4) , Alain H. Fuchs (4)

1 PASTEUR - Processus d'Activation Sélective par Transfert d'Energie Uni-électronique ou Radiatif (UMR 8640)
2 SIEN - Systèmes interfaciaux à l'echelle nanometrique
3 ILV - Institut Lavoisier de Versailles
4 ENSCP - Ecole Nationale Supérieure de Chimie de Paris - Chimie ParisTech-PSL

MOFs come alive: The combination of gas‐adsorption experiments at various temperatures with an osmotic thermodynamic model produced a generic temperature–loading phase diagram that displays unexpected re‐entrant behavior. The breathing effect in the metal–organic framework MIL‐53(Al) is predicted to be general and should be observed over a limited temperature range regardless of the guest adsorbate.

Domaines: Chimie théorique et/ou physique; Matériaux

Anne Boutin, Marie-Anne Springuel-Huet, Andrei Nossov, Antoine Gedeon, Thierry Loiseau, et al.. Breathing transitions in MIL-53(Al) metal-organic framework upon xenon adsorption.. Angewandte Chemie International Edition, 2009, 48 (44), pp.8314-7. ⟨10.1002/anie.200903153⟩. ⟨hal-00548070⟩