Microstructural Investigation of the Aging Behavior of (3Y-TZP)Al2O3 Composites
Résumé
The low-temperature autoclave aging behavior of zirconia-toughened alumina composites processed by a classical powder mixing processing route was analyzed using atomic force microscopy (AFM), scanning electron microscopy, and X-ray diffraction (XRD). The transformation was evaluated in terms of nucleation and growth, assessed by XRD. The timetemperature equivalency of the transformation was used to measure an apparent activation energy of the nucleation stage of the transformation of 78 kJ/mol. The microstructural features influencing the transformation were identified, and the influence of the alumina matrix on the transformation was investigated. Transformation progression grain by grain was observed by AFM. Transformation does not only occur in zirconia agglomerates but also in isolated zirconia grains. The matrix could partially inhibit the transformation. This behavior could be rationalized considering the constraining effect of the alumina matrix, shape strain accommodation arguments, and microstructural homogeneity effects.