Fracture of 6056 aluminum sheet materials : effect of specimen thickness and hardening behavior on strain localization and toughness

Alexandra Asserin-Lebert (1) , Jacques Besson (1) , Anne-Françoise Gourgues (1)

1 CDM - Centre des Matériaux

The roles of specimen thickness and hardening behavior of the material on the ductile tearing resistance of a 6056 aluminum alloy are investigated separately as a function of stress triaxiality, by varying both the heat treatment (overaging or annealing + slow cooling) and the specimen geometry. The fracture path can be slanted or flat. Results show that increasing hardening capability and specimen thickness favors flat fracture. For the overaged material, the energy dissipation rate, measured on Kahn specimens, reaches a maximum value for an intermediate value of thickness (3.2 mm), whereas for the annealed material, a change in the fracture mode (from slanted to flat) induces a continuous increase in toughness with increasing thickness up to 6 mm.

Mots clés: Aluminum alloy 6056; Ductile rupture; Fracture mechanisms; Strain hardening; Specimen thickness effect

Domaines: Science des matériaux [cond-mat.mtrl-sci]

Alexandra Asserin-Lebert, Jacques Besson, Anne-Françoise Gourgues. Fracture of 6056 aluminum sheet materials : effect of specimen thickness and hardening behavior on strain localization and toughness. Materials Science and Engineering: A, 2005, 395 (1-2), pp.186-194. ⟨10.1016/j.msea.2004.12.018⟩. ⟨hal-00151590⟩