Volatiana Razafindramanana (1) , Stéphane Gorsse (1) , Jacques Huot (2) , Jean-Louis Bobet (1)

1 ICMCB - Institut de Chimie de la Matière Condensée de Bordeaux
2 UQTR - Université du Québec à Trois-Rivières

The alloy TiFe has interesting hydrogen storage properties for practical applications: low cost, operation at room temperature, and good hydrogen capacity. However, the first hydrogenation is difficult and increases the cost of the alloy. In this work, we studied the effect of adding hafnium to TiFe in order to enhance the first hydrogenation process. TiFe + x Hf alloys, with x = 0, 4, 8, 12, and 16 wt.%, were synthesized by arc melting. The microstructure of the as-cast alloys was investigated by scanning electron microscopy and electron microprobe analysis. These alloys consisted of B2-TiFe, C14-Laves, and BCC (Body Centered Cubic) phases. A minimum of 8 wt.% of hafnium is required to obtain an enhancement of the first hydrogenation. In the first hydrogenation, the material reaches its maximal hydrogen capacity in less than two hours at room temperature and under 20 bars of hydrogen. Hafnium addition also had the effect of lowering the plateau pressure in the pressure-composition isotherm. It could be concluded that hafnium has a positive effect on the activation properties of TiFe.

Mots clés: hafnium addition; hydrogen storage; first hydrogenation; TiFe alloy

Domaines: Matériaux

Volatiana Razafindramanana, Stéphane Gorsse, Jacques Huot, Jean-Louis Bobet. Effect of hafnium addition on the hydrogenation process of TiFe alloy. Energies, 2019, 12 (18), pp.3477. ⟨10.3390/en12183477⟩. ⟨hal-02309259⟩