Crystal chemistry of a new solid solution in the BaO-Bi2O3-Nb2O5 system : Ba5x/2Bi(1-x)5/3Nb5O15
Résumé
A solid solution of the type Ba5x/2Bi(1-x)5/3Nb5O15 has been identified in the BaO-Bi2O3-Nb2O5 system for the first time. The limits of the solid solution are within the range 0.52 <= x <= 0.80. The compositions x = 0.52, 0.60, 0.72, 0.77, 0.78, and 0.80 were synthesized by the solid-state technique from the starting materials in stoichiometric quantities. The powder X-ray patterns of all the phases in the domain indicate a structural similarity to tetragonal tungsten bronzes (TTBs). The compositions below x = 0.52 and those above x = 0.80 exhibit barium niobate and bismuth niobate impurities, respectively. Single crystals of the composition x = 0.77 were obtained by the melt cooling technique. The crystal structure of Ba3.85/2Bi1.15/3Nb5O15 (x = 0.77) was solved in the tetragonal space group P4bm (No. 100) with a = 12.4938 (14) angstrom, c = 3.9519 (2) A, V = 616.87 (10) angstrom(3), and Z = 2 and was refined to an R index of 0.034. Dielectric measurements on all the phases indicate a typical relaxor behavior with a broad phase transition at T-m approximate to 300 K.