High Temperature Properties of TiCN-Mo2C-Co Cermets Studied by Mechanical Spectroscopy

Abstract : Low frequency internal friction measurements were performed on TiC0.7N0.3-Mo2C-Co cermets in an inverted torsion-pendulum working with forced oscillations. A thermally activated high temperature background and three thermally activated peaks were observed in the internal friction spectra. Two peaks, which are stable during thermal treatments, appear (at 1 Hz) at about 1050 K and 1200 K respectively. The third peak, appearing at about 950 K, is only observed during the first heating of the as-received samples. In order to locate the relaxation phenomena, similar measurements were performed on carbide-carbonitride skeletons, in which the metallic binder phase was chemically removed. Complementary microstructural characterizations, performed by conventional TEM, allow one to identify the physical mechanisms responsible for the IF peaks and background.
Type de document :
Article dans une revue
Journal de Physique IV Colloque, 1996, 06 (C8), pp.C8-751-C8-754. 〈10.1051/jp4:19968163〉
Liste complète des métadonnées

Littérature citée [3 références]  Voir  Masquer  Télécharger

https://hal.archives-ouvertes.fr/jpa-00254598
Contributeur : Archives Journal de Physique <>
Soumis le : lundi 1 janvier 1996 - 08:00:00
Dernière modification le : vendredi 18 mai 2018 - 11:28:02
Document(s) archivé(s) le : jeudi 20 mai 2010 - 19:33:48

Fichier

ajp-jp4199606C8163.pdf
Accord explicite pour ce dépôt

Identifiants

Collections

AJP

Citation

G. Feusier, Thierry Cutard, C. Verdon, T. Viatte, W. Benoit. High Temperature Properties of TiCN-Mo2C-Co Cermets Studied by Mechanical Spectroscopy. Journal de Physique IV Colloque, 1996, 06 (C8), pp.C8-751-C8-754. 〈10.1051/jp4:19968163〉. 〈jpa-00254598〉

Partager

Métriques

Consultations de la notice

123

Téléchargements de fichiers

124