Plastic deformation of LiNbO3 single crystals
Résumé
High temperature (> 0.8 TM) plastic deformation of ferroelectric monodomain LiNbO3 single crystals is reported. Different stress orientations have been chosen and basal, prismatic and pyramidal glide planes could be activated. A detailed analysis of the glide elements is made by means of optical, chemical etching and X-ray topography observations, as well as mechanical considerations (CRSS). The basal glide system (0001) <1210> with a CRSS of 13 MPa seems easier to activate than the prismatic glide system {1120} <1101> whose CRSS is 15 MPa, the pyramidal glide system {1102} <1101> with a CRSS of 17-18 MPa being the hardest to activate.
Mots clés
dislocation etching
ferroelectric materials
lithium compounds
slip
X ray diffraction examination of materials
high temperature
prismatic glide
critical resolved shear stress
optical studies
plastic deformation
ferroelectric monodomain
pyramidal glide
chemical etching
X ray topography
basal glide
LiNbO sub 3 single crystals