DEPENDENCE OF ELASTIC MODULUS ON MICROSTRUCTURE IN 2090-TYPE ALLOYS

M. O' Dowd , W. Ruch , E. Starke , Jr.

The Young's modulus, shear modulus and Poisson's ratio were determined using an ultrasonic puise echo technique. Three commercially fabricated aluminum-copper-lithium alloys and an aluminum-lithium binary alloy were examined. The elastic properties were measured as a function of aging time, aging temperature, amount of stretching and testing direction. An increase in Young's modulus due to delta prime and T1 precipitation has been measured and treated quantitatively including precipitation kinetics. A significant decrease of about 5% in the modulus of elasticity was found in the peak age condition. This decrease can be attributed to precipitation of the T2 phase. The shear modulus behaves similar to Young's modulus while the Poisson's ratio remains unchanged. There is no significant orientation dependence of the elastic properties on testing direction despite the fact that a typical. rolling texture was present.

Domaines: Articles anciens

M. O' Dowd, W. Ruch, E. Starke, Jr.. DEPENDENCE OF ELASTIC MODULUS ON MICROSTRUCTURE IN 2090-TYPE ALLOYS. Journal de Physique Colloques, 1987, 48 (C3), pp.C3-565-C3-576. ⟨10.1051/jphyscol:1987366⟩. ⟨jpa-00226597⟩