The effect of size on the strength of FCC metals at elevated temperatures: annealed copper

Jeffrey M. Wheeler (1, 2) , Christoph Kirchlechner (3, 4) , Jean-Sebastien Micha (5) , Johann Michler (1) , Daniel Kiener (4)

1 EMPA Mechanics of Materials and Nanostructures
2 Laboratory for Nanometallurgy [ETH Zürich]
3 Structure and Nano-/Micromechanics Materials Department
4 MU - University of Leoben
5 ESRF - European Synchrotron Radiation Facility

As the length scale of sample dimensions is reduced to the micron and sub-micron scales, the strength of various materials has been observed to increase with decreasing size, a fact commonly referred to as the 'sample size effect'. In this work, the influence of temperature on the sample size effect in copper is investigated using in situ microcompression testing at 25, 200 and 400 degrees C in the SEM on vacuum-annealed copper structures, and the resulting deformed structures were analysed using X-ray mu Laue diffraction and scanning electron microscopy. For pillars with sizes between 0.4 and 4 mu m, the size effect was measured to be constant with temperature, within the measurement precision, up to half of the melting point of copper. It is expected that the size effect will remain constant with temperature until diffusion-controlled dislocation motion becomes significant at higher temperatures and/or lower strain rates. Furthermore, the annealing treatment of the copper micropillars produced structures which yielded at stresses three times greater than their un-annealed, FIB-machined counterparts

Mots clés: Size effect; copper; high temperature deformation; mu-Laue diffraction