Where is the glass transition temperature of poly(tetrafluoroethylene)? A new approach by dynamic rheometry and mechanical tests

Gérard Calleja (1) , Alex Jourdan (2) , Bruno Ameduri (1) , Jean-Pierre Habas (1)

1 ICGM ICMMM - Institut Charles Gerhardt Montpellier - Institut de Chimie Moléculaire et des Matériaux de Montpellier
2 AREVA

Polytetrafluoroethylene (PTFE) has been used for many years in different application fields due to its outstanding chemical and physical properties. But, the value of its glass transition temperature is still today a matter of controversy and very different values are proposed in the literature. This paper proposes to answer to this scientific question using dynamic mechanical measurements. First, the viscoelastic properties of PTFE are described on a large temperature range and the influence of the shearing frequency is carefully investigated. Then, the effects produced by the polymer annealing on its thermomechanical behavior are detailed. This study comforts the idea that PTFE amorphous phase should be considered as comprised of two distinct regions. The first one named "mobile amorphous fraction" (MAF) is able to relax at low temperature (T = −103 °C). The other one is specific of the macromolecular segments present at the boundaries between crystalline and amorphous domains. Due to the close vicinity of the crystallites, these macromolecular segments present a more restricted mobility. The corresponding phase is designated as the "rigid amorphous fraction" (RAF) and its mechanical relaxation produces itself at higher temperature (T = 116 °C). Actually, this latter value is strongly dependent on the material crystallinity degree. In particular, it is shifted to higher temperature after occurrence of a recrystallization that is accompanied by a further reduction of the RAF's dynamic. Instead, the characteristics of the MAF relaxation are poorly affected. Tensile tests also support that the "real" Tg of the polymer is located at low temperature. All these results have been compared to those of the literature to propose a real scientific discussion and to understand the origin of somewhat contradictory interpretations.

Mots clés: Annealing; Dynamic mechanical measurements; Glass transition temperature; Mobile amorphous fraction; PTFE; Relaxation

Domaines: Polymères

Gérard Calleja, Alex Jourdan, Bruno Ameduri, Jean-Pierre Habas. Where is the glass transition temperature of poly(tetrafluoroethylene)? A new approach by dynamic rheometry and mechanical tests. European Polymer Journal, 2013, 49 (8), pp.2214-2222. ⟨10.1016/j.eurpolymj.2013.04.028⟩. ⟨hal-00844535⟩