Nanostructures Defined by The Local Oxidation of Ferromagnetic GaMnAs Layer

Voves J. Voves J. (1) , Zbynek Soban (1) , Michal Jelinek (1) , Volodimir Komarnickij (1) , Miroslav Cukr (2) , Vit Novak (2)

1 Dept. of Microelectronics
2 Department of Surfaces and Interfaces

The results of Local Anodic Oxidation (LAO) on the thin GaMnAs layers are reported. The ferromagnetic GaMnAs layers were prepared by low temperature MBE growth in a Veeco Mod Gen II machine. The LAO process was performed with the AFM microscope Smena NT-MDT placed in the sealed box with the controlled humidity in the range 45-80%. The oxide was grown in the semi-contact mode of the AFM. Sample was positively biased with respect to the AFM tip with the bias from 6 to 24 V. The conductive diamond coated AFM tips with the radius 30 nm were utilized for the oxidation. The tip speed during the oxidation was changed from 400 nm/s to 1.5 μm/s. The tip force was also changed during the oxidation. The height of oxide nanolines increases with applied voltage from 3 to 18 nm. The width of these lines was approximately 100 nm at half of the maximum.

Domaines: Science des matériaux [cond-mat.mtrl-sci]

Voves J. Voves J., Zbynek Soban, Michal Jelinek, Volodimir Komarnickij, Miroslav Cukr, et al.. Nanostructures Defined by The Local Oxidation of Ferromagnetic GaMnAs Layer. ENS 2007, Dec 2007, Paris, France. pp.85-90. ⟨hal-00202518⟩