Hydrothermal synthesis of nanosized BaTiO3 powders and dielectric properties of corresponding ceramics - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Solid State Sciences Année : 2005

Hydrothermal synthesis of nanosized BaTiO3 powders and dielectric properties of corresponding ceramics

Résumé

BaTiO3 fine powders were synthesized by hydrothermal method at 150 °C or 250 °C for 7 h, starting from a mixture of TiCl3 + BaCl2 or TiO2 + BaCl2. The size of the crystallites is close to 20 nm whatever the starting mixture and the reaction temperature. These powders are well crystallized and constituted of a mixture of the metastable cubic and stable tetragonal phases. The ceramics obtained after uniaxial pressing and sintering at 1250 °C for 10 h or 20 h present high densification (up to 99.8%). The Curie temperature (Tc) and the electrical permittivity ( r) of the ceramics strongly depend on the type of titanium source that has been used for preparing the powder and on the sintering dwell time. Particularly, Tc is shifted towards lower temperature when TiCl3 is used. The permittivity value at Tc of BaTiO3 sintered at 1250 °C for 10 h reaches 7000 and 11,000 with respectively TiCl3 and TiO2 used as titanium source.

Domaines

Matériaux
Fichier principal
Vignette du fichier
boulos_341.pdf (576.47 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03601642 , version 1 (08-03-2022)

Identifiants

Citer

Madona Boulos, Sophie Guillemet, François Mathieu, Bernard Durand, Thierry Lebey, et al.. Hydrothermal synthesis of nanosized BaTiO3 powders and dielectric properties of corresponding ceramics. Solid State Sciences, 2005, 176 (13-14), pp.1301-1309. ⟨10.1016/j.ssi.2005.02.024⟩. ⟨hal-03601642⟩
227 Consultations
17 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More