Fluidized-Bed Chemical Vapor Deposition of Silicon on Very Dense Tungsten Powder

Abstract : A very dense tungsten powder was coated by silicon from silane using the fluidized-bed chemical vapor deposition process. A reactor of reduced diameter was developed in order to decrease the weight of powders treated. Results show that the fluidization of this powder is possible in this reactor, but with non-optimal gas solid contact induced by the high powder density. Important disturbances of the fluidized-bed temperatures appeared in the presence of silane, due to a partial bed defluidization related to the cohesive nature of the deposit. These disturbances are clearly exacerbated by the exceptional density of the particles. This is probably why a powder agglomeration has been unavoidable when the bed temperature was too low and/or the silane inlet concentration too high. However, a set of operating parameters could be found, allowing a uniform and continuous coating of the whole powder surface.
Document type :
Journal articles
Complete list of metadata

https://hal.archives-ouvertes.fr/hal-03464691
Contributor : Open Archive Toulouse Archive Ouverte (OATAO) Connect in order to contact the contributor
Submitted on : Friday, December 3, 2021 - 1:42:15 PM
Last modification on : Wednesday, June 1, 2022 - 4:02:35 AM
Long-term archiving on: : Friday, March 4, 2022 - 7:04:20 PM

File

vanni_14446.pdf
Files produced by the author(s)

Identifiers

Collections

Citation

Florence Vanni, Mélanie Montaigu, Brigitte Caussat, Carine Ablitzer, Xavière Iltis, et al.. Fluidized-Bed Chemical Vapor Deposition of Silicon on Very Dense Tungsten Powder. Chemical Engineering Technology, 2015, 38 (7), pp.1254-1260. ⟨10.1002/ceat.201400350⟩. ⟨hal-03464691⟩

Share

Metrics

Record views

4

Files downloads

13