Nanostructure in Fe0.65Cr0.35 close to the upper limit of the miscibility gap

Contents lists available at ScienceDirect

Résumé

The nanostructure of an Fe0.65Cr0.35 alloy has been investigated by atom probe tomography after highprecision thermal treatments close to the upper limit of the miscibility gap (MG). It is found that the wavelength of the decomposed ferrite between Cr-and Fe-rich regions grows exponentially when approaching the upper limit of the MG. Furthermore, the nanostructure change is gradual with temperature indicating a narrow metastable region and a diffuse transition out of the spinodal regime. Atomistic modelling near the limit of instability further supports the experimental observations. The findings are discussed in relation to the Cahn-Hilliard theory.
Fichier principal
Vignette du fichier
135 Scripta Materialia 180 (2020) 62–65 NANOSTRUCTURE IN Fe65Cr35 CLOSE TO THE UPPER LIMIT OF THE MISCIBILITY GAP, A. DAHLSTRÖM, F. DANOIX, P. HEDSTRÖM, J. ODQVIST, H. ZAPOLSKY.pdf (985.3 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03365846 , version 1 (05-10-2021)

Identifiants

Citer

Alexander Dahlström, Frederic Danoix, Peter Hedström, Joakim Odqvist, Helena Zapolsky. Nanostructure in Fe0.65Cr0.35 close to the upper limit of the miscibility gap. Scripta Materialia, 2020, 180, pp.62-65. ⟨10.1016/j.scriptamat.2020.01.024⟩. ⟨hal-03365846⟩
24 Consultations
17 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More