Iron-iron oxide supported palladium catalyst for the interconversion of formate and carbon dioxide

Wei-Jyun Wang (1) , Frankie Roberts (1) , Stena Peterson (1) , Su Ha (1) , Louis Scudiero (1) , Romain Coustel (2) , Martine Mallet (2) , Mustapha Abdelmoula (2) , Christian Ruby (2)

1 WSU - Washington State University
2 LCPME - Laboratoire de Chimie Physique et Microbiologie pour les Matériaux et l'Environnement

Synthesized palladium-coated iron-iron oxide (Fe@FeOx/Pd) nanoparticles (NPs) using the successive salt reduction method are tested for their activity and stability toward formate oxidation (FO) and electrochemical CO2 reduction to formate (eCO2RF). The experimental results for FO show a current density at 0.12 V vs. Ag/AgCl of 1.65 mA/cm2 over 1 h, which is 16 times higher than that for Pd NPs. Furthermore, the same catalyst displays a higher current density with a faradaic efficiency (FE) of 95.6 % toward the eCO2RF, and exhibits a lower degree of CO adsorption. The iron-iron oxide interaction with the overlayer palladium is characterized by TEM/EDX, XPS/UPS, Mössbauer spectroscopy, and electrochemical techniques such as cyclic voltammetry (CV) and chronoamperometry (CA). NMR is used to estimate the amount of formate produced by the eCO2RF. A positive binding energy shift of the Pd 3d peak and the upshift of the d-band center as measured by XPS compared to monometallic homemade Pd NPs confirm that the electronic perturbation of the catalyst surface plays a major role in enhancing the performance of Fe@FeOx/Pd for both FO and eCO2RF. Furthermore, the work function as measured by UPS for the Fe@FeOx/Pd material is lower than that for monometallic Pd confirming a change in chemical properties of the catalyst surface. Finally, Mössbauer spectroscopy is used to determine the composition, structure and nature of all sites of the Fe@FeOx substrate before use and the perturbation of their intrinsic properties by the Pd overlayer. This change in intrinsic properties of the Pd coated material provides additional explanations for the electrochemical improvement measured for this catalyst toward both FO and eCO2RF

Mots clés: Iron/iron oxide-palladium; TEM; XPS; UPS; Mössbauer; CV; CA; NMR; formate oxidation and electrochemical CO2 reduction

Domaines: Catalyse

Wei-Jyun Wang, Frankie Roberts, Stena Peterson, Su Ha, Louis Scudiero, et al.. Iron-iron oxide supported palladium catalyst for the interconversion of formate and carbon dioxide. Chemical Engineering Journal, 2022, 427, pp.131763. ⟨10.1016/j.cej.2021.131763⟩. ⟨hal-03329171⟩