Cobalt-mediated radical (co)polymerization of vinyl chloride and vinyl acetate

Résumé

The cobalt mediated radical polymerization (CMRP) of vinyl chloride (VC) in the presence of bis(acetylacetonato)cobalt(II) (Co(acac)2) as a controlling agent is presented for the first time. Using an alkyl-Co(III) compound (R0–(CH2–CHOAc)<4–Co(acac)2; R0 = (H3C)2(OCH3)C–CH2–C(CH3)(CN)–) as an initiator, the bulk polymerization under non-isotherm conditions is controlled. 1H NMR spectra of the resulting PVC show that the CMRP process does not significantly affect the level of defects compared to a PVC prepared by a conventional free radical polymerization at the same temperature. Using the same alkyl-cobalt(III) compound, the copolymerization of VC and VAc is controlled at 40 °C provided that enough VAc (about 40 mol%) is present in the polymerization medium to moderate the VC polymerization. In line with reactivity ratios, VC is preferentially incorporated in the polymer at the early stages of the polymerization, leading to copolymers with a high VC content at moderate conversions. This is the first report of a CMRP of VC and of the synthesis of well-defined statistical PVC-co-PVAc copolymers by this technique.
Fichier principal
Vignette du fichier
311-10.1039-C2PY20413D-Accepted.pdf (1.12 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03156049 , version 1 (02-03-2021)

Identifiants

Citer

Yasmine Piette, Antoine Debuigne, Christine Jérôme, Vincent Bodart, Rinaldo Poli, et al.. Cobalt-mediated radical (co)polymerization of vinyl chloride and vinyl acetate. Polymer Chemistry, 2012, 3 (10), pp.2880-2891. ⟨10.1039/C2PY20413D⟩. ⟨hal-03156049⟩
45 Consultations
126 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More