Thermodynamic data of adsorption reveal the entry of CH$_4$ and CO$_2$ in a smectite clay interlayer
Résumé
The ability of smectite clays to incorporate gases in their interlayers is shown to be conditioned by interlayer spacing, depending, in turn, on phyllosilicate layer composition and effective size of the charge-balancing cations. As illustrated by earlier in situ X-ray diffraction and spectroscopic characterization of the gas/clay interface, most smectites with small-size charge-balancing cations, such as Na+ or Ca2+, accommodate CO2 and CH4 in their interlayers only in a partially hydrated state resulting in the opening of the basal spacing, above a certain critical value. In the present study CH4 and CO2 adsorption isotherms were measured for Naand Mg-exchanged montmorillonite up to 9 MPa using a manometric technique. The process of dehydration of these clays was thoroughly characterized by thermogravimetric analysis and powder X-ray diffraction. A dramatic decrease in specific surface area and methane and carbon dioxide adsorption capacities for fully dehydrated samples in comparison to partially dehydrated ones is assigned to the shrinkage of interlayer spacing resulting in its inaccessibility for the entry of CH4 and CO2 molecules. This observation is direct evidence of CH4 and CO2 adsorption capacity variation depending on the opening of smectite clay interlayer spacing.