Surface Roughness Based Characterization of Slip Band for Damage Initiation in a Nickel Base Superalloy

Résumé

This work presents a computational protocol, based on a variance analysis integrated with the bootstrap method, to investigate surface damage resulting from localization of plastic deformation in slip bands of a Ni-base superalloy. For assessment of fatigue crack initiation, surface roughness is introduced to quantify the degree of slip irreversibility. The contribution of this study is to provide a most relevant roughness parameter that can extract the salient features of slip bands within damaged grains, and thus enabling the discrimination of damaged and undamaged grains for description of fatigue-induced surface damage. Results suggest that the maximum peak height ( S p ) is the most relevant parameter. And a very pronounced variability of S p values is observed for damaged grains

Dates et versions

hal-02889620 , version 1 (04-07-2020)

Identifiants

Citer

Hsin Shen Ho, Marion Risbet, Xavier Feaugas, Maxence Bigerelle, Erliang Zhang. Surface Roughness Based Characterization of Slip Band for Damage Initiation in a Nickel Base Superalloy. Materials Science, 2018, 24 (1), ⟨10.5755/j01.ms.24.1.17684⟩. ⟨hal-02889620⟩
28 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More