Enhanced Piezoelectric Response in Nanostructured Ni/PVDF Films

M Melilli (1) , D Gorse (1) , A Galifanova (1) , O Oral (1) , E Balanzat (2) , Olivier Doaré , M Tabellout (3) , Mikhael Bechelany (4) , D Lairez (1, 5) , Je Wegrowe (1) , Mary Claude Clochard (1)

1 LSI - Laboratoire des Solides Irradiés - Irradiated Solids Laboratory
2 CIMAP - UMR 6252 - Centre de recherche sur les Ions, les MAtériaux et la Photonique
3 UM - Le Mans Université
4 IEM - Institut Européen des membranes
5 LLB - UMR 12 - Laboratoire Léon Brillouin

Poly(vinylidene fluoride) (PVDF) composites have recently emerged as excellent candidates to fabricate flexible and small piezoelectric generators for portable devices. Among various techniques used to nanostructure polarized PVDF, the track-etching represents a new route for manufacturing nanostructured composite thin films. The moderate influence of irradiation on the piezoelectric response of polarized PVDF makes possible the use of this technique. In this way, a nanostructured composite based on polarized thin PVDF films comprising embedded nickel nanowires (Ni NWs) was fabricated. The nanostructured PVDF/Ni NWs composites were tested under bending conditions using a homemade pressure cell. Due to the presence of NWs, an increase of five-fold the initial dielectric permittivity, in the low-frequency range, was observed. It suggested the presence of an interfacial polarization at the PVDF/Ni interface. With respect to the etched PVDF, the nanostructured PVDF/Ni NWs composites exhibited a non-negligible enhancement by 2.5 times the piezoelectric efficiency. This result was attributed to the increased Au/Ni NWs electrode surface.

Mots clés: Swift heavy ion irradiation; Track-etching; Piezoelectric polymer; Nanowires; Composite; Nanostructuration; Swift heavy ion irradiation