Characterization of intergranular corrosion defects in a 2024 T351 aluminium alloy

Résumé

Intergranular corrosion defects formed after a 24h immersion in a 1M NaCl solution in a 2024-T351 Al alloy were characterized using a combination of electron microscopy techniques. Results showed the dissolution of intergranular Cu-rich precipitates all along the corroded grain boundaries. Cu species were incorporated inside the amorphous alumina oxide film identified in the corroded grain boundaries leading to the formation of structural defects in the oxide film. A 10–200nm-thin metallic Cu-rich layer was also observed at the oxide/metal interface and at the tip of the intergranular corrosion defect.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Bonfils-Lahovary_25560.pdf (1.73 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02497140 , version 1 (03-03-2020)

Identifiants

Citer

Marie-Laëtitia De Bonfils-Lahovary, Lydia Laffont, Christine Blanc. Characterization of intergranular corrosion defects in a 2024 T351 aluminium alloy. Corrosion Science, 2017, 119, pp.60-67. ⟨10.1016/j.corsci.2017.02.020⟩. ⟨hal-02497140⟩
31 Consultations
105 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More