Caryophyllene as a Precursor of Cross-Linked Materials

Abstract : This paper aims at the synthesis of a new type of elastomers from caryophyllene. The adopted strategy was to cross-link the polycaryophyllene, which was synthesized by ring-opening metathesis polymerization (ROMP). The polycaryophyllene obtained showed Mn = 2 x 104 g.mol-1 (Đ = 1.5) with a glass transition temperature (Tg) of -35 °C. On the first hand, thermal cross-linking was performed in the presence of organic peroxides or sulfur system. On the second hand, thiol-ene coupling initiated by UV-light at room temperature was also investigated as an alternative pathway to cross-link the polycaryophyllene. The materials obtained were analyzed by TGA, DSC, and DMA. The Tg of cross-linked polycaryophyllene could be easily modulated from -35 °C to a range between -25 and 10 °C by changing the type of cross-linking agent. The curing process led to the improvement of thermal stability ranging from 200 °C to around 340 °C. Finally, the network storage modulus varied from 1 to 100 MPa at room temperature.
Complete list of metadata

Cited literature [39 references]  Display  Hide  Download

https://hal.archives-ouvertes.fr/hal-02471294
Contributor : Etienne Grau <>
Submitted on : Friday, February 7, 2020 - 10:27:54 PM
Last modification on : Monday, November 16, 2020 - 11:54:01 AM
Long-term archiving on: : Friday, May 8, 2020 - 6:25:27 PM

File

Publi.pdf
Files produced by the author(s)

Identifiers

Collections

Citation

Etienne Grau, Anderson M. M. S. Medeiros, Cédric Le Coz. Caryophyllene as a Precursor of Cross-Linked Materials. ACS Sustainable Chemistry & Engineering, American Chemical Society, 2020, ⟨10.1021/acssuschemeng.9b07413⟩. ⟨hal-02471294⟩

Share

Metrics

Record views

115

Files downloads

341