Electrodeposition, characterization and corrosion behaviour of tin-20 wt.% zinc coatings electroplated from a non-cyanide alkaline bath

Sébastien Dubent (1, 2) , Marc L.A.D. Mertens (3) , M. Saurat (2)

1 PIMM - Laboratoire Procédés et Ingénierie en Mécanique et Matériaux
2 CNAM - Conservatoire National des Arts et Métiers [CNAM]
3 Chercheur indépendant

Tin-zinc alloy electroplated coatings are recognized as a potential alternative to toxic cadmium as corrosion resistant deposits because they combine the barrier protection of tin with the cathodic protection afforded by zinc. The coatings containing 20 wt.% zinc, balance tin, offer excellent corrosion protection for steel and do not form gross voluminous white corrosion products like pure zinc or high zinc alloy deposits. In this study, the effects of variables of the process (i.e. cathodic current density, pH and temperature) on deposit composition have been evaluated using a Hull cell to obtain 20 wt.% zinc alloy coatings. The tin-20 wt.% zinc deposits, produced with electroplating optimized conditions, were characterized by scanning electron microscopy (SEM), energy dispersive X-ray spectrometry (EDS), X-ray fluorescence spectrometry (XRF) and glow discharge optical emission spectrometry (GDOES). On the other hand, the corrosion behaviour of tin-zinc alloy electroplated coatings on steel has been investigated using electrochemical methods in a 3 wt.% NaCl solution and the salt spray test. The performance of the deposits was compared with cadmium and zinc-nickel electrodeposited coatings. The results show that the corrosion resistance of tin-20 wt.% zinc alloy coating is superior to that of cadmium and zinc-12 wt.% nickel coatings. Finally, sliding friction tests were conducted.

Mots clés: Alloy coatings; Cadmium; Corrosion; Electrodeposition; Morphology; Salt spray test; Spectrometry; Tin-zinc

Domaines: Matériaux

Sébastien Dubent, Marc L.A.D. Mertens, M. Saurat. Electrodeposition, characterization and corrosion behaviour of tin-20 wt.% zinc coatings electroplated from a non-cyanide alkaline bath. Materials Chemistry and Physics, 2010, 120 (2-3), pp.371-380. ⟨10.1016/j.matchemphys.2009.11.017⟩. ⟨hal-02458179⟩