Ultrafine versus coarse grained Al 5083 alloys: From low-cycle to very-high-cycle fatigue

Meng Li (1, 2) , Anchal Goyal (2) , Véronique Doquet (2) , Nicolas Ranc (3) , Jean-Philippe Couzinié (4)

1 Shanghai Jiao Tong University [Shanghai]
2 LMS - Laboratoire de mécanique des solides
3 PIMM - Laboratoire Procédés et Ingénierie en Mécanique et Matériaux
4 ICMPE - Institut de Chimie et des Matériaux Paris-Est

The fatigue performance of coarse and ultrafine-grained (UFG) 5083 Al alloy were compared, from low to very high cycle fatigue. The UFG alloy exhibited cyclic hardening and predominant kinematic hardening. At high plastic strain amplitude (and only in this regime), it showed easier crack initiation and a lower fatigue resistance. Its resistance to HCF was hardly better than that of its coarse grained counterpart until 2.10 6 cycles, but 43% higher in VHCF, until 5.10 8 cycles. Beyond that point, internal crack initiation occurred, and the fatigue resistance of the UFG material decreased, which was explained using Fracture Mechanics.

Mots clés: Cyclic plasticity; Fish-eye; VHCF; Ultrafine grains; Al-Mg alloy

Domaines: Mécanique des matériaux [physics.class-ph]

Meng Li, Anchal Goyal, Véronique Doquet, Nicolas Ranc, Jean-Philippe Couzinié. Ultrafine versus coarse grained Al 5083 alloys: From low-cycle to very-high-cycle fatigue. International Journal of Fatigue, 2019, 121, pp.84-97. ⟨10.1016/j.ijfatigue.2018.12.004⟩. ⟨hal-02063493⟩