Volume Variation Process of High-Density Polyethylene During Tensile and Creep Tests

F. Addiego (1) , A. Dahoun (1) , C. G'Sell (1) , J. M. Hiver (2)

1 INPL - Institut National Polytechnique de Lorraine
2 LPM - Laboratoire de physique des matériaux

Samples of high-density polyethylene have been subjected to tensile tests and creep experiments by means of a video-controlled testing system (VidéoTraction ©). The evolution of specific volume in this semi-crystalline polymer is determined versus true strain. In the elastic stage, we measure a hydrostatic expansion and then, in the plastic stage, we observe a competition between a compaction effect and a dilatation phenomenon. Although compaction is probably overestimated in the present testing technique, it represents a pertinent mechanism that is ascribed to the orientation of the amorphous chains during stretching. This phenomenon is characterized by X-ray diffraction measurements that show a reduction of average distance between amorphous chains. Dilatation process is explained by the diminution of crystallinity and by the formation, growth and coalescence of crazes inside and between spherulites. Electron microscopy reveals these defects. The competition between compaction and dilatation, controlled by the mobility of the amorphous phase, depends on temperature and time.

Domaines: Physique [physics]

F. Addiego, A. Dahoun, C. G'Sell, J. M. Hiver. Volume Variation Process of High-Density Polyethylene During Tensile and Creep Tests. Oil & Gas Science and Technology - Revue d'IFP Energies nouvelles, 2006, 61 (6), pp.715-724. ⟨10.2516/ogst:2006009⟩. ⟨hal-02005892⟩