Effects of the fundamental oxide properties on the electric field-flash temperature during flash sintering

Résumé

Flash sintering of oxide powders is associated with dissipated power in the narrow range 10–50 W·cm−3 irrespective of their composition. By analysis and normalization of the experimental results from literature to constant particle size (100 nm) and applied electric field (500 V cm−1), we show that the relative flash sintering temperature is dictated by the oxide crystal-type and its cation ionic potential resulting from its chemical composition. The expected flash onset temperature increases with the increase in fusion enthalpy and confirm the formation of liquid at the particle contacts as a mechanism for the powder densification.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Chaim_21694.pdf (489.46 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01999298 , version 1 (30-01-2019)

Identifiants

Citer

Rachman Chaim, Claude Estournès. Effects of the fundamental oxide properties on the electric field-flash temperature during flash sintering. Scripta Materialia, 2019, 163, pp.130-132. ⟨10.1016/j.scriptamat.2019.01.018⟩. ⟨hal-01999298⟩
36 Consultations
47 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More