Influence of the microstructure on the corrosion behaviour of 2024 aluminium alloy coated with a trivalent chromium conversion layer

Résumé

The influence of 2024 aluminium alloy microstructure on the protective properties of trivalent chromium process (TCP) coatings was studied: samples aged at 190 °C were analysed by comparison to a T3 state. The surface Cu coverage after deoxidation was higher for long-aged samples because nanometer scale Cu-rich precipitates formed during ageing behaved as distinct electrochemical entities and contributed to the formation of copper deposits. The growth mechanisms and kinetics of TCP coatings were directly related to the surface Cu coverage: thicker but more defective TCP coatings formed on long-aged samples leading to the lowest anti-corrosion properties.
Fichier principal
Vignette du fichier
Saillard_21412.pdf (669.58 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01989678 , version 1 (22-01-2019)

Identifiants

Citer

Romain Saillard, Bernard Viguier, Grégory Odemer, Alessandro Pugliara, Benoit Fori, et al.. Influence of the microstructure on the corrosion behaviour of 2024 aluminium alloy coated with a trivalent chromium conversion layer. Corrosion Science, 2018, 142, pp.119-132. ⟨10.1016/j.corsci.2018.07.007⟩. ⟨hal-01989678⟩
28 Consultations
110 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More