Impact of machine stiffness on ‘‘pop-in’’ crack propagation instabilities

Tom Petit (1, 2) , Claire Ritter (2) , Jacques Besson (1) , Thilo F. Morgeneyer (1)

1 CDM - Centre des Matériaux
2 SEMI - Service d'Etudes des Matériaux Irradiés

This study investigates ‘‘pop-in’’ phenomenon, i.e. unstable but limited crack propagation associated with a sudden decrease in load. Its origin is linked to an interaction between material tearing modulus and machine stiffness. Small scale yielding criterion for instability is applied to compact tension (CT) samples. To validate this criterion experimentally, firstly tests are performed on aluminum alloy with various tearing moduli. Secondly the effect of mechanical loading on pop-in behavior is studied by varying machine stiffness using an innovative setup. Pop-ins are shown to be mechanical instabilities due to interaction between material tearing modulus and system stiffness.

Mots clés: J-integral; Toughness testing; Unstable crack growth; Ductile fracture; 6061

Domaines: Science des matériaux [cond-mat.mtrl-sci]

Tom Petit, Claire Ritter, Jacques Besson, Thilo F. Morgeneyer. Impact of machine stiffness on ‘‘pop-in’’ crack propagation instabilities. Engineering Fracture Mechanics, 2018, 202, pp.405-422. ⟨10.1016/j.engfracmech.2018.08.007⟩. ⟨hal-01915471⟩