Effects of Selective Laser Melting additive manufacturing parameters of Inconel 718 on porosity, microstructure and mechanical properties - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials Science and Engineering: A Année : 2018

Effects of Selective Laser Melting additive manufacturing parameters of Inconel 718 on porosity, microstructure and mechanical properties

K. Moussaoui
Walter Rubio
Michel Mousseigne
T. Sultan
  • Fonction : Auteur
Farhad Rezai-Aria

Résumé

The effect of SLM parameters on porosity, microstructure and mechanical properties is studied. To this purpose, the Selective Laser Melting (SLM) technology is applied to manufacture Inconel 718 specimens. The material, the manufacturing process, the Hot Isostatic Pressure (HIP), heat treatment, observation procedures and characterisation of mechanical properties are presented. A columnar-dendritic microstructure was observed on all the SLM specimens and a Volumetric Energy Density (VED) effect on the latter was also noted. The rate of porosity varies in relation to the VED and is considerably reduced after HIP. The heat treatment erases the dendritic microstructure, significantly enhances microhardness and confers on the alloy tensile mechanical properties comparable to forged Inconel 718.
Fichier principal
Vignette du fichier
effects-of-selective-laser-melting.pdf (4.38 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01867274 , version 1 (15-11-2018)

Identifiants

Citer

K. Moussaoui, Walter Rubio, Michel Mousseigne, T. Sultan, Farhad Rezai-Aria. Effects of Selective Laser Melting additive manufacturing parameters of Inconel 718 on porosity, microstructure and mechanical properties. Materials Science and Engineering: A, 2018, 735, pp.182 - 190. ⟨10.1016/j.msea.2018.08.037⟩. ⟨hal-01867274⟩
323 Consultations
2326 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More