Relationship between the volume of the unit cell of hexagonal-close-packed Ti, hardness and oxygen content after α-case formation in Ti–6Al–2Sn–4Zr–2Mo–0.1Si alloy

Abstract : In this study, the influence of oxygen diffusion on the physical properties of Ti–6Al–2Sn–4Zr–2Mo–0.1Si was examined. Measurements were carried out directly on sample cross sections which were preoxidized at high temperature. The lattice parameter evolution was measured using synchrotron X-ray diffraction and was coupled with microhardness and electron probe microanalyzer results with the aim of highlighting their relationships. The results show that the hardness and oxygen gradients along the oxygen diffusion zone in the alloy are similar to the evolution of the [alpha]α-phase unit-cell volume quantified by X-ray diffraction. Linear relationships were found between these three parameters.
Document type :
Journal articles
Complete list of metadatas

https://hal.archives-ouvertes.fr/hal-01755484
Contributor : Open Archive Toulouse Archive Ouverte (oatao) <>
Submitted on : Friday, March 30, 2018 - 3:54:46 PM
Last modification on : Friday, June 14, 2019 - 6:31:18 PM

File

Baillieux_19741.pdf
Publisher files allowed on an open archive

Identifiers

Collections

Citation

Jean Baillieux, Dominique Poquillon, Benoît Malard. Relationship between the volume of the unit cell of hexagonal-close-packed Ti, hardness and oxygen content after α-case formation in Ti–6Al–2Sn–4Zr–2Mo–0.1Si alloy. Journal of Applied Crystallography, International Union of Crystallography, 2016, 49 (1), pp.175-181. ⟨10.1107/S1600576715022906⟩. ⟨hal-01755484⟩

Share

Metrics

Record views

69

Files downloads

118