Heterojunction p-Cu2O/ZnO-n solar cell fabricated by spark plasma sintering

Abstract : Cuprous oxide and zinc oxide nanoparticles were prepared at room temperature by inorganic polycondensation. X-ray diffraction (XRD) analyses show that the oxide phases formed are pure and well crystallized. The spark plasma sintering (SPS) technique was successfully used to prepare dense nanoceramics with superimposed layers of Cu2O and ZnO nanopowders. Sintering conditions were optimized to densify the ceramics without phase transformation or diffusion. These ceramics were also characterized by XRD and scanning electron microscopy (SEM), as well as X-ray computed tomography (XCT). SEM and XCT showed that nanograins are preserved after SPS throughout both oxide materials, while a smaller layer (*20 lm) of pure oxide phase with larger grains is formed in between Cu2O and ZnO during the sintering process. The SPS technique results in high material density, with the absence of porosity and cracks, homogenous distribution, and a good phase separation. This is the first time that such as-prepared dense oxide-based heterojunction exhibits a photovoltaic effect under illumination opening a new route for preparing solar cells.
Complete list of metadatas

https://hal.archives-ouvertes.fr/hal-01754855
Contributor : Open Archive Toulouse Archive Ouverte (oatao) <>
Submitted on : Friday, March 30, 2018 - 11:15:04 AM
Last modification on : Friday, January 10, 2020 - 9:08:24 PM

File

tenailleau_19790.pdf
Publisher files allowed on an open archive

Identifiers

Collections

Citation

Christophe Tenailleau, Guillaume Salek, Thi Ly Le, Benjamin Duployer, Jean-Jacques Demai, et al.. Heterojunction p-Cu2O/ZnO-n solar cell fabricated by spark plasma sintering. Materials for Renewable and Sustainable Energy, Springer, 2017, 6 (4), pp.18. ⟨10.1007/s40243-017-0102-8⟩. ⟨hal-01754855⟩

Share

Metrics

Record views

157

Files downloads

177