On deformation and damage micromechanisms in strong work hardening 2198 T3 aluminium alloy

Abstract : The deformation and damage micromechanisms ahead of a notch in a large flat specimen have been assessed using in situ synchrotron laminography combined with digital volume correlation for the strain evaluation in the material bulk. Despite the enhanced work hardening of the naturally aged Al-Cu-Li alloy several slanted strained bands were found from very early loading onward in the slanted fracture region. The final slanted crack followed one of the strained bands without significant ductile damage growth. In the high stress triaxiality region, close to the notch that underwent substantial local necking, two damage micromechanisms were observed, namely, i) limited void nucleation and growth from intermetallic particles, and ii) slanted shear cracks, even starting from the specimen surface and also located in single grains as shown by post mortem EBSD analyses. In the intermediate region a new deformation mechanism of flip-flopping strain bands and resulting flip- flopping cracks have been revealed using 'projection DIC' measurements.
Type de document :
Article dans une revue
Acta Materialia, Elsevier, 2018, 149, pp.29-45. 〈10.1016/j.actamat.2018.01.026〉
Liste complète des métadonnées

Littérature citée [56 références]  Voir  Masquer  Télécharger

https://hal.archives-ouvertes.fr/hal-01710066
Contributeur : François Hild <>
Soumis le : mardi 27 mars 2018 - 15:48:04
Dernière modification le : lundi 12 novembre 2018 - 11:04:14
Document(s) archivé(s) le : jeudi 13 septembre 2018 - 10:21:56

Fichier

ACMA2018-ccsd.pdf
Fichiers produits par l'(les) auteur(s)

Identifiants

Citation

Ante Buljac, François Hild, Lukas Helfen, Thilo Morgeneyer. On deformation and damage micromechanisms in strong work hardening 2198 T3 aluminium alloy. Acta Materialia, Elsevier, 2018, 149, pp.29-45. 〈10.1016/j.actamat.2018.01.026〉. 〈hal-01710066〉

Partager

Métriques

Consultations de la notice

188

Téléchargements de fichiers

53