Accelerated Aging in 3‐mol%‐Yttria‐Stabilized Tetragonal Zirconia Ceramics Sintered in Reducing Conditions

José F Bartolomé 1 Isabel Montero 1 Marcos Díaz 1 Sonia López‐esteban 1 José S Moya 1 Sylvain Deville 2 Laurent Gremillard 2 Jérome Chevalier 2 Gilbert Fantozzi 2
1 ICMM - Instituto de Ciencia de Materiales de Madrid
2 MATEIS - Matériaux, ingénierie et science [Villeurbanne]
Abstract : The aging behavior of 3‐mol%‐yttria‐stabilized tetragonal zirconia (3Y‐TZP) ceramics sintered in air and in reducing conditions was investigated at 140°C in water vapor. It was observed by X‐ray diffraction (XRD) that 3Y‐TZP samples sintered in reducing conditions exhibited significantly higher tetragonal‐to‐monoclinic transformation than samples with similar density and average grain size values but obtained by sintering in air. This fact is explained by the increase of the oxygen vacancy concentration and by the presence at the grain boundary region of a new aggregate phase formed because of the exolution of Fe2+ ions observed by X‐ray photoelectron spectroscopy.
Type de document :
Article dans une revue
Journal of the American Ceramic Society, Wiley, 2004, 87 (12), pp.2282-2285. 〈10.1111/j.1151-2916.2004.tb07505.x〉
Liste complète des métadonnées

Littérature citée [23 références]  Voir  Masquer  Télécharger
https://hal.archives-ouvertes.fr/hal-01670890
Contributeur : Laboratoire Mateis <>
Soumis le : jeudi 17 mai 2018 - 09:41:56
Dernière modification le : samedi 27 octobre 2018 - 01:21:15
Document(s) archivé(s) le : lundi 24 septembre 2018 - 13:53:28

Fichier

Accelerated Aging in 3‐mol...
Fichiers produits par l'(les) auteur(s)

Identifiants

Collections

INSA-LYON | UNIV-LYON1

Citation

José F Bartolomé, Isabel Montero, Marcos Díaz, Sonia López‐esteban, José S Moya, et al.. Accelerated Aging in 3‐mol%‐Yttria‐Stabilized Tetragonal Zirconia Ceramics Sintered in Reducing Conditions. Journal of the American Ceramic Society, Wiley, 2004, 87 (12), pp.2282-2285. 〈10.1111/j.1151-2916.2004.tb07505.x〉. 〈hal-01670890〉

Exporter

BibTeX TEI DC DCterms EndNote

Partager

Métriques

Consultations de la notice

87

Téléchargements de fichiers

23

Contact

support.ccsd.cnrs.fr
hal.support@ccsd.cnrs.fr
Logo CCSD