Surface and mechanical properties of transparent polycrystalline YAG fabricated by SPS

Résumé

YAG powder was synthesised by reverse-strike co-precipitation, calcined at 1000°C and dispersed by either ball-milling with α-alumina (BMA) or zirconia (BMz) spheres or by ultrasonication (US). All the dispersed powders were consolidated by SPS to nearly theoretical density, but only the US powder gave rise to a transparent material (transmittance of about 60% at 600 nm, 1 mm thickness), characterised by an ultra-fine microstructure (average size of 330nm). In the BM materials, Raman spectroscopy allowed to evidence some phonon vibrational shifts due to secondary phases deriving from pollution by the milling media, not detectable by XRD because present in small amounts. The transmittance of the as-sintered US sample was further increased by annealing in air at 900°C; this was assigned to the restoration of some oxygen vacancies created in the reducing environment of the SPS chamber, as evidenced by XPS (X-ray photoelectron spectroscopy). Finally, US samples sintered in the 1250–1400°C were submitted to a basic mechanical characterisation, showing a very good hardness, in spite of a moderate fracture toughness, especially for the fully dense and fine-grained materials sintered at 1300–1350°C.
Fichier principal
Vignette du fichier
Palmero2013.pdf (536.88 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01670836 , version 1 (11-10-2022)

Licence

Paternité - Pas d'utilisation commerciale

Identifiants

Citer

Paola Palmero, Barbara Bonelli, Gilbert Fantozzi, Giulia Spina, Guillaume Bonnefont, et al.. Surface and mechanical properties of transparent polycrystalline YAG fabricated by SPS. Materials Research Bulletin, 2013, 48 (7), pp.2589-2597. ⟨10.1016/j.materresbull.2013.03.003⟩. ⟨hal-01670836⟩
51 Consultations
34 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More