Influence of surface and internal casting defects on the fatigue behaviour of A357‐T6 cast aluminium alloy

Résumé

The influence of internal casting defects on the fatigue properties of A357-T6 alloy has been studied. Specimens with artificial casting defects ( mm) placed at the surface or in the bulk have been produced. A reference S–N curve has been obtained for the material containing only natural defects (microshrinkages). Cycling has been performed in air or under vacuum. In spite of their relatively large size, the internal artificial defects do not induce a reduction of the fatigue life compared to the reference material. When the artificial defects are placed at the surface, a decrease is observed when the specimens are cycled in air but it disappears again when cycling is performed in vacuum conditions. The detrimental effect of the casting defects is discussed in relation to their ability to initiate a crack growing in vacuum or not. It can be concluded that the increased fatigue lives observed for internal defects are the consequence of slower crack initiation and propagation mechanism occurring in vacuum.
Fichier non déposé

Dates et versions

hal-01669932 , version 1 (21-12-2017)

Identifiants

Citer

I Serrano‐munoz, Jean-Yves Buffiere, Catherine Verdu, Y Gaillard, P Mu, et al.. Influence of surface and internal casting defects on the fatigue behaviour of A357‐T6 cast aluminium alloy. International Journal of Fatigue, 2016, 82, pp.361--370. ⟨10.1016/j.ijfatigue.2015.07.032⟩. ⟨hal-01669932⟩
131 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More